ชื่อสินค้า : ผงฟลักซ์เชื่อม Co-Ni-Cr-B-Si alloy and tungsten carbide. 50% tungsten carbides.

ยี่ห้อ : Castolin Eutectic

รุ่น : Eutalloy® 10611

Eutalloy® 10611 (UltrAloy) is a micro-pulverised cobalt-nickel-chromium alloy with a high concentration of Diamax particles. It has been developed for protective coating of parts which must provide exceptionally high resistance to abrasion and erosion. Thanks to a special matrix composition Eutalloy® 10611 makes it possible to protectively coat steel, stainless steel and cast iron parts working in temperatures of up to 700°C, providing at the same time excellent corrosion resistance.

Anti-wear composition:
There are two essential components to this alloy, the matrix and the hard-phase Diamax particles, both micropulverised.
The Co-Ni-Cr matrix of Eutalloy® 10611 is dense with special tungsten carbide hard particles, providing extra wear resistance.
The matrix has a hardness of ~55 HRC. The polygonal-shaped, tungsten carbide Diamax particles have a hardness of approx. 1900 HV.
Excellent resistance to low/medium-pressure abrasion, fine-particle erosion, also against impact. The special matrix composition ensures wear resistance up to 700°C, providing at the same time excellent corrosion resistance.

Base metals: For stainless, cast and other steels, and cast iron.

Cost-effective process:
Used with a Eutalloy® system torch, the Eutalloy® 10611 alloy ensures coatings of smooth and uniform quality. The result is far superior to those obtained with conventional processes, saving the user on finish machining and other labour costs.

Features and benefits
- Excellent resistance to abrasion under severe pressure
- Good resistance to erosion, impact and corrosion
- Retains wear-resistant properties at high temperatures
- Applied by simultaneous spray/fusion-process, using SuperJet Eutalloy S torch

Applications
Protective coatings for extrusion screws, mould orifices, scraper blades, mixer blades, fan blades.

Technical data:
Service temperature (max.) ~700ºC
Hardness (matrix) ~55 HRC
Hardness (hard phases) ~1900 HV